Method for Producing Polymer Film

ABSTRACT

A method for producing a polymer film is disclosed herein. The method is capable of effectively forming a polymer film on a substrate, where the polymer film comprises highly aligned block copolymers without orientation defects, coordination number defects, distance defects, and the like. The method can be applied to production of various patterned substrates.

CROSS-REFERENCE TO RELATED APPLICATION(S)

The present application is a continuation of International Application No. PCT/KR2017/013731, filed on Nov. 29, 2017, which claims priority to Korean Patent Application No. 10-2016-0162129, filed on Nov. 30, 2016, the disclosures of which are incorporated herein by reference.

TECHNICAL FIELD

The present application relates to a method for producing a polymer film.

BACKGROUND ART

A block copolymer has a molecular structure in which polymer blocks having different chemical structures are linked via covalent bonds. The block copolymer can form a periodically arranged structure such as a sphere, a cylinder or a lamella by phase separation. The domain shape and size of the structure formed by a self-assembly phenomenon of the block copolymer can be extensively controlled by, for example, the kind of the monomer forming each block or the relative ratios between the blocks, and the like.

Due to these properties, the block copolymer is being considered for application to nanowire production, production of various next-generation nano devices such as quantum dots or metal dots, or a lithography method capable of forming high-density patterns on a predetermined substrate, and the like.

The technique of adjusting orientation of the self-assembled structure of the block copolymer horizontally or vertically on various substrates occupies a very large proportion in practical application of the block copolymer. Typically, the orientation of nanostructures in the film of the block copolymer is determined by which block of the block copolymer is exposed to the surface or air. In general, since a number of substrates have polarity and air is non-polar, a block having a larger polarity among the blocks of the block copolymer is wetted to the substrate, and a block having a smaller polarity is wetted at the interface with air. Therefore, there is a demand for a technique such that the blocks having different characteristics of the block copolymer are simultaneously wetted to the substrate side.

DISCLOSURE

In this specification, the term alkyl group may mean an alkyl group having 1 to 20 carbon atoms, 1 to 16 carbon atoms, 1 to 12 carbon atoms, 1 to 8 carbon atoms or 1 to 4 carbon atoms, unless otherwise specified. The alkyl group may be a linear, branched or cyclic alkyl group, which may be optionally substituted with one or more substituents.

In this specification, the term alkoxy group may mean an alkoxy group having 1 to 20 carbon atoms, 1 to 16 carbon atoms, 1 to 12 carbon atoms, 1 to 8 carbon atoms or 1 to 4 carbon atoms, unless otherwise specified. The alkoxy group may be a linear, branched or cyclic alkoxy group, which may be optionally substituted with one or more substituents.

The term alkenyl group or alkynyl group herein means an alkenyl group or alkynyl group having 2 to 20 carbon atoms, 2 to 16 carbon atoms, 2 to 12 carbon atoms, 2 to 8 carbon atoms or 2 to 4 carbon atoms, unless otherwise specified. The alkenyl or alkynyl group may be linear, branched or cyclic, which may be optionally substituted with one or more substituents.

The term alkylene group herein may mean an alkylene group having 1 to 20 carbon atoms, 1 to 16 carbon atoms, 1 to 12 carbon atoms, 1 to 8 carbon atoms or 1 to 4 carbon atoms, unless otherwise specified. The alkylene group may be a linear, branched or cyclic alkylene group, which may be optionally substituted with one or more substituents.

The term alkenylene group or alkynylene group herein may mean an alkenylene group or alkynylene group having 2 to 20 carbon atoms, 2 to 16 carbon atoms, 2 to 12 carbon atoms, 2 to 8 carbon atoms or 2 to 4 carbon atoms. The alkenylene group or alkynylene group may be linear, branched or cyclic, which may be optionally substituted with one or more substituents.

The term aryl group or arylene group herein may mean, unless otherwise specified, a monovalent residue or divalent residue derived from a compound comprising one benzene structure, or a structure in which two or more benzene rings are linked while sharing one or two carbon atoms, or linked by any linker, or a derivative thereof. The aryl group or arylene group may be, for example, an aryl group having 6 to 30 carbon atoms, 6 to 25 carbon atoms, 6 to 21 carbon atoms, 6 to 18 carbon atoms or 6 to 13 carbon atoms, unless otherwise specified.

In the present application, the term aromatic structure may mean the aryl group or arylene group.

In this specification, the term alicyclic ring structure means a cyclic hydrocarbon structure other than an aromatic ring structure, unless otherwise specified. The alicyclic ring structure may be, for example, an alicyclic ring structure having 3 to 30 carbon atoms, 3 to 25 carbon atoms, 3 to 21 carbon atoms, 3 to 18 carbon atoms or 3 to 13 carbon atoms, unless otherwise specified.

In the present application, the term single bond may mean a case where no separate atom is present at the relevant site. For example, in the structure represented by A-B-C, when B is a single bond, no separate atom exists at the site represented by B, and A and C are directly connected, so that it may mean to form a structure represented by A-C.

In the present application, the substituent, with which the alkyl group, alkenyl group, alkynyl group, alkylene group, alkenylene group, alkynylene group, alkoxy group, aryl group, arylene group, chain or aromatic structure, and the like may be optionally substituted, may be exemplified by a hydroxy group, a halogen atom, a carboxyl group, a glycidyl group, an acryloyl group, a methacryloyl group, an acryloyloxy group, a methacryloyloxy group, a thiol group, an alkyl group, an alkenyl group, an alkynyl group, an alkylene group, an alkenylene group, an alkynylene group, an alkoxy group or an aryl group, and the like, but is not limited thereto.

The present application relates to a method for producing a polymer film. The polymer film of the present application may be applied to a method for producing a patterned substrate. The method for producing the patterned substrate of the present application may be performed by a lithography method in which a directed self-assembly material is applied as a template, where the directed self-assembly material may be a block copolymer.

The method for producing a polymer film of the present application allows a self-assembled structure of the directed self-assembly material to be formed with higher precision in the process of producing the patterned substrate as above, thereby precisely performing patterning of the substrate. In particular, the present application can effectively form a structure, such as a sphere, a cylinder or a lamella, as the self-assembled structure, and effectively form such a structure in a vertically oriented state. In the present application, the term vertical orientation indicates the orientation of the block copolymer, where the orientation of the phase separation structure or the self-assembled structure formed by the block copolymer may mean an orientation perpendicular to the substrate direction, and for example, may mean a case where the interface between the domain formed by a polymer segment A and the domain formed by a polymer segment B, which are described below, of the block copolymer is perpendicular to the surface of the substrate. In the present application, the term vertical is an expression in consideration of an error, which may be a meaning including, for example, errors within ±10 degrees, ±8 degrees, ±6 degrees, ±4 degrees or ±2 degrees.

The production method of the present application may comprise a step of inducing the self-assembled structure of the block copolymer in the polymer film comprising the block copolymer. Here, the polymer film may comprise the block copolymer as a main component. For example, the proportion of the block copolymer inside the polymer film may be 60% or more, 70% or more, 80% or more, 90% or more, or 95% or more, by weight. The proportion of the block copolymer in the polymer film can be, for example, 100% or less by weight.

The block copolymer may comprise a polymer segment A, and a polymer segment B different from the polymer segment A.

In the present application, the fact that two kinds of polymer segments are identical means any one case of cases in which in any two kinds of polymer segments the kinds of monomer units contained as the main component are identical to each other, or 50% or more, 55% or more, 60% or more, 65% or more, 70% or more, 75% or more, 80% or more, 85% or more or 90% or more of monomer unit kinds contained in two kinds of polymer segments are common and a weight ratio deviation of the common monomer units in each polymer segment is within 30%, within 25%, within 20%, within 20%, within 15%, within 10% or within 5%. Here, the monomer unit that the polymer segment comprises as a main component is a monomer unit in which 60% or more, 65% or more, 70% or more, 75% or more, 80% or more, 85% or more, or 90% or more is included and 100% or less is included in the corresponding polymer segment. If both polymer segments do not satisfy the two cases, they are polymer segments that are different from each other. Here, it may be proper that the ratio of the common monomer units is satisfied for both polymer segments. For example, if any polymer segment 1 has monomer units of A, B, C, D and F and the other polymer segment 2 has monomer units of D, F, G and H, then the common monomer units in polymer segments 1 and 2 are D and F, where in the position of polymer segment 1 the common ratio is 40% (=100×2/5) because two kinds of the total five kinds are common, but in the position of polymer segment 2 the ratio is 50% (=100×2/4). Thus, in this case, both polymer segments may be regarded as not identical because the common ratio is not less than 50% only in polymer segment 2. On the other hand, the weight ratio deviation of the common monomers is a percentage of a numerical value in which a large weight ratio minus a small weight ratio is divided by the small weight ratio. For example, in the above case, if the weight ratio of the D monomer units in the segment 1 is about 40% based on 100% of the total weight ratio of the whole monomer units in the segment 1 and the weight ratio of the D monomer units in the segment 2 is about 30% based on 100% of the total weight ratio of the whole monomer units in the segment 2, the weight ratio deviation may be about 33% (=100×(40-30)/30) or so. If the common monomer units are two or more kinds in two segments, in order to be the same segment, it can be considered as the common monomers when the weight ratio deviation within 30% is satisfied for all the common monomers or for the monomer unit as the main component. Each polymer segment that is recognized as the same by the above criteria may be a different type of polymer (e.g., any one segment is in the form of a block copolymer and the other segment is in the form of a random copolymer), but it may be, suitably, the same type of polymer.

The respective polymer segments of the block copolymer may be formed by only one monomer, or may be formed by two or more of monomers. The block copolymer may be a diblock copolymer comprising only one polymer segment A and one polymer segment B. The block copolymer may also be a block copolymer of three blocks or more which comprises each one of the polymer segments A and B, and further comprises any one or both of the polymer segments A and B, or further comprises other polymer segments rather than the polymer segments A and B.

The specific kind of the block copolymer to be applied in the production method of the present application is not particularly limited as long as it comprises the polymer segment A and the polymer segment B different from each other as above, where any kind of block copolymer known to be capable of forming the self-assembled structure can be applied.

For example, as the block copolymer, a block copolymer may be used, which comprises, as the polymer segments A and B, a polyvinyl pyrrolidone segment, a polyalkyl (meth)acrylate segment such as polymethyl methacrylate, a polylactic acid segment, a polyvinyl pyridine segment, a polystyrene segment such as polystyrene or polytrimethylsilylstyrene, a polyalkylene oxide segment such as polyethylene oxide, a polybutadiene segment, a polyisoprene segment or a polyolefin segment such as polyethylene, and the like.

The block copolymer comprises two or more polymer segments connected by covalent bonds, and thus phase separation occurs and a so-called self-assembled structure is formed. The present inventors have confirmed that the block copolymer can be more effectively applied to the production method by satisfying any one or two or more of conditions to be described below. Accordingly, the block copolymer of the present application may satisfy at least one of the following conditions. The conditions described below are in parallel, and any one condition does not override the other conditions. The block copolymer may satisfy any one condition selected from the conditions described below, or may satisfy two or more conditions. Through the fulfillment of any one condition, the block copolymer can exhibit more effectively vertical orientation in the process of producing the polymer film as described above.

An exemplary block copolymer of the present application comprises a polymer segment A and a polymer segment B different from the polymer segment A, wherein the block copolymer or the polymer segment A may exhibit a melting transition peak or an isotropic transition peak in a range of −80° C. to 200° C. in a DSC analysis (Condition 1).

An exemplary block copolymer of the present application comprises a polymer segment A and a polymer segment B different from the polymer segment A, wherein the block copolymer or the polymer segment A may exhibit a peak having a half-value width in a range of 0.2 to 0.9 nm⁻¹ within a scattering vector (q) range of 0.5 nm⁻¹ to 10 nm⁻¹ upon an XRD analysis (Condition 2).

An exemplary block copolymer of the present application comprises a polymer segment A and a polymer segment B different from the polymer segment A, wherein the polymer segment A may comprise a side chain and the number (n) of chain-forming atoms in the side chain and the scattering vector (q) obtained by the XRD analysis of the polymer segment A may satisfy Equation 1 below (Condition 3).

3 nm⁻¹ to 5 nm⁻¹ =nq/(2×π)  [Equation 1]

In Equation 1, n is a number of chain-forming atoms of the side chain, and q is the smallest scattering vector (q) in which the peak is observed in the X-ray diffraction analysis for the polymer segment containing the side chain, or the scattering vector (q) in which the peak of the largest peak area is observed.

An exemplary block copolymer of the present application comprises a polymer segment A and a polymer segment B different from the polymer segment A, wherein the absolute value of the difference between the surface energy of the polymer segment A and the surface energy of the polymer segment B may be 10 mN/m or less (Condition 4).

An exemplary block copolymer of the present application comprises a polymer segment A and a polymer segment B different from the polymer segment A, wherein the absolute value of the difference in density between the polymer segment A and the polymer segment B may be 0.25 g/cm³ or more (Condition 5).

In the respective block copolymers, the polymer segment A may be a polymer segment comprising a side chain as described below.

Hereinafter, each of the conditions will be described in detail.

In this specification, physical properties, such as density, that can be changed by temperature are values measured at room temperature, unless otherwise specified. The term room temperature is a natural temperature without warming or cooling, which may mean a temperature of about 10° C. to 30° C., about 25° C. or about 23° C.

A. Condition 1

The block copolymer of the present application or any one polymer segment of the block copolymer may exhibit a melting transition peak or isotropic transition peak in a range of −80° C. to 200° C. in a DSC (differential scanning calorimetry) analysis. The block copolymer or any one polymer segment of the block copolymer may also exhibit only any one peak of the melting transition peak or the isotropic transition peak, or may exhibit both of the two peaks. Such a block copolymer may be a copolymer exhibiting a crystal phase and/or a liquid crystal phase suitable for self-assembly as a whole or comprising a polymer segment exhibiting such a crystal phase and/or a liquid crystal phase. The polymer segment satisfying Condition 1 above may be a polymer segment A.

The block copolymer exhibiting the above-described DSC behavior or any one polymer segment of the block copolymer may further satisfy the following conditions.

For example, when the isotropic transition peak and the melting transition peak appear simultaneously, the difference (Ti−Tm) between the temperature (Ti) at which the isotropic transition peak appears and the temperature (Tm) at which the melting transition peak appears may be in a range of 5° C. to 70° C. In another example, the difference (Ti−Tm) may be 10° C. or more, 15° C. or more, 20° C. or more, 25° C. or more, 30° C. or more, 35° C. or more, 40° C. or more, 45° C. or more, 50° C. or more, 55° C. or more, or 60° C. or more. The block copolymer having a difference (Ti−Tm) between the temperature (Ti) of the isotropic transition peak and the temperature (Tm) of the melting transition peak in the above range or the block copolymer comprising such a polymer segment can maintain excellent phase separation or self-assembly characteristics.

In another example, when the isotropic transition peak and the melting transition peak appear simultaneously, the ratio (M/I) of the area (I) of the isotropic transition peak and the area (M) of the melting transition peak may be in a range of 0.1 to 500. In the DSC analysis, the block copolymer having a ratio (M/I) of the area (I) of the isotropic transition peak and the area (M) of the melting transition peak in the above range or the block copolymer comprising such a polymer segment can maintain excellent phase separation or self-assembly characteristics. In another example, the ratio (M/I) may be 0.5 or more, 1 or more, 1.5 or more, 2 or more, 2.5 or more, or 3 or more. In another example, the ratio (M/I) may be 450 or less, 400 or less, 350 or less, 300 or less, 250 or less, 200 or less, 150 or less, 100 or less, 90 or less, or 85 or less.

A method of performing the DSC analysis is known, and in the present application, the above analysis can be performed by such a known method.

The temperature (Tm) range at which the melting transition peak appears may be a range of −10° C. to 55° C. In another example, the temperature (Tm) may be 50° C. or less, 45° C. or less, 40° C. or less, 35° C. or less, 30° C. or less, 25° C. or less, 20° C. or less, 15° C. or less, 10° C. or less, 5° C. or less, or 0° C. or less.

The block copolymer may comprise a polymer segment having a side chain, as described below. In this case, the block copolymer may satisfy Equation 2 below.

−10≤Tm−12.25° C.×n+149.5≤10  [Equation 2]

In Equation 2, Tm is a temperature at which a melting transition peak of the block copolymer or the polymer segment having the side chain appears, and n is a number of chain-forming atoms of the side chain.

The block copolymer satisfying Equation above may have excellent phase separation or self-assembly properties.

In another example, Tm−12.25° C.×n+149.5 in Equation 2 may be −8 to 8, −6 to 6, or about −5 to 5 or so.

B. Condition 2

The block copolymer of the present application may comprise a polymer segment showing at least one peak in a predetermined range of the scattering vector (q) upon the XRD analysis (X-ray diffraction analysis). The polymer segment satisfying Condition 2 may be the polymer segment A.

For example, any one polymer segment of the block copolymer may exhibit at least one peak in a scattering vector (q) range of 0.5 nm⁻¹ to 10 nm⁻¹ in the X-ray diffraction analysis. In another example, the scattering vector (q) at which the peak appears may be 0.7 nm⁻¹ or more, 0.9 nm⁻¹ or more, 1.1 nm⁻¹ or more, 1.3 nm⁻¹ or more, or 1.5 nm⁻¹ or more. In another example, the scattering vector (q) at which the peak appears may be 9 nm⁻¹ or less, 8 nm⁻¹ or less, 7 nm⁻¹ or less, 6 nm⁻¹ or less, 5 nm⁻¹ or less, 4 nm⁻¹ or less, 3.5 nm⁻¹ or less, or 3 nm⁻¹ or less. The half-value width (full width at half maximum, FWHM) of the peak identified in the above scattering vector (q) range may be in the range of 0.2 to 0.9 nm⁻¹. In another example, the half-value width may be 0.25 nm⁻¹ or more, 0.3 nm⁻¹ or more, or 0.4 nm⁻¹ or more. In another example, the half-value width may be 0.85 nm⁻¹ or less, 0.8 nm⁻¹ or less, or 0.75 nm⁻¹ or less.

In Condition 2, the term half-value width may mean a width of the peak (the difference in the scattering vector (q)) at a position showing the ½ intensity of the maximum peak intensity.

The scattering vector (q) and the half-value width in the XRD analysis are values obtained by a numerical analytical method in which the results obtained by the XRD analysis to be described below are applied by a least-square method. In the method, the profile of the XRD patterns is subjected to Gaussian fitting in a state where a portion showing the smallest intensity in the XRD diffraction patterns is taken as a baseline and the intensity in the above is set to zero, and then the scattering vector and the half-value width can be obtained from the fitted results. The R square at the time of Gaussian fitting is at least 0.9 or more, 0.92 or more, 0.94 or more, or 0.96 or more. A method capable of obtaining the information as above from the XRD analysis is known, and for example, a numerical analysis program such as origin can be applied.

The polymer segment showing the peak of the half-value width in the above scattering vector (q) range may comprise a crystalline site suitable for self-assembly. The block copolymer comprising the polymer segment identified in the above-described scattering vector (q) range may exhibit excellent self-assembly properties.

The XRD analysis can be performed by transmitting X-rays to a sample and then measuring the scattering intensity according to the scattering vector. The XRD analysis can be performed using a polymer prepared by polymerizing only a monomer constituting any one polymer segment of the block copolymer, for example, the polymer segment A. The XRD analysis can be performed on such a polymer without any special pretreatment, and for example, can be performed by drying the polymer under appropriate conditions and then passing it through X-rays. As the X-ray, an X-ray having a vertical size of 0.023 mm and a horizontal size of 0.3 mm can be applied. The scattering vector and the half-value width can be obtained by obtaining as an image 2D diffraction patterns that are scattered in the sample and exited using a measuring instrument (for example, 2D marCCD), and fitting the obtained diffraction pattern with the above-described manner.

C. Condition 3

The block copolymer of the present application may comprise, as the polymer segment A, a polymer segment having a side chain to be described below, wherein the number (n) of chain-forming atoms of the side chain can satisfy Equation 1 below with the scattering vector (q) obtained by the X-ray diffraction analysis performed in the same manner as in Condition 2 above.

3 nm⁻¹ to 5 nm⁻¹ =nq/(2×π)  [Equation 1]

In Equation 1, n is a number of the chain-forming atoms, and q is the smallest scattering vector (q) in which the peak is observed in the X-ray diffraction analysis for the polymer segment containing the side chain, or the scattering vector (q) in which the peak of the largest peak area is observed. Also, in Equation 1, π means the circular constant.

The scattering vector or the like introduced into Equation 1 is a value obtained by the same manner mentioned in the above-described X-ray diffraction analysis method.

The scattering vector (q) introduced in Equation 1 may be, for example, a scattering vector (q) in a range of 0.5 nm⁻¹ to 10 nm⁻¹. In another example, the scattering vector (q) introduced into Equation 1 may be 0.7 nm⁻¹ or more, 0.9 nm⁻¹ or more, 1.1 nm⁻¹ or more, 1.3 nm⁻¹ or more, or 1.5 nm⁻¹ or more. In another example, the scattering vector (q) introduced into Equation 1 above may be 9 nm⁻¹ or less, 8 nm⁻¹ or less, 7 nm⁻¹ or less, 6 nm⁻¹ or less, 5 nm⁻¹ or less, 4 nm⁻¹ or less, 3.5 nm⁻¹ or less, or 3 nm⁻¹ or less.

When a polymer composed of only the polymer segment comprising the side chain of the block copolymer has formed a film, Equation 1 shows a relationship of the distance (D) between the polymer main chains containing the side chains and the number of chain-forming atoms in the side chain, and when the number of chain-forming atoms of the side chain in the polymer having the side chain satisfies Equation 1 above, the crystallinity represented by the side chain is increased, whereby the phase separation property or the vertical orientation can be significantly improved. In another example, the nq/(2×π) according to Equation 1 above may also be 4.5 nm⁻¹ or less. Here, the distance (D, unit: nm) between the polymer main chains in which the side chains are contained can be calculated by the equation D=2×π/q, where D is the distance (D, unit: nm), and π and q are as defined in Equation 1.

D. Condition 4

The absolute value of the difference between the surface energy of the polymer segment A and the surface energy of the polymer segment B in the block copolymer of the present application may be 10 mN/m or less, 9 mN/m or less, 8 mN/m or less, 7.5 mN/m or less, or 7 mN/m or less. The absolute value of the difference in surface energy may be 1.5 mN/m, 2 mN/m or 2.5 mN/m or more. The structure in which the polymer segments A and B having the absolute value of the difference in surface energy in this range are connected by covalent bonds can induce effective microphase separation. Here, the polymer segment A may be, for example, a polymer segment having a side chain as described below.

The surface energy can be measured using a drop shape analyzer (DSA100 product from KRUSS). Specifically, the surface energy can be measured for a film in which a coating liquid obtained by diluting a target sample (block copolymer or homopolymer), which is measured, in fluorobenzene to a solid concentration of about 2 weight %, is coated on a substrate to a thickness of about 50 nm and a coating area of 4 cm² (width: 2 cm, height: 2 cm), and dried at room temperature for about 1 hour, and then subjected to thermal annealing at 160° C. for about 1 hour. The process of dropping the deionized water whose surface tension is known on the film subjected to the thermal annealing and obtaining the contact angle thereof is repeated five times to obtain an average value of the obtained five contact angle values, and identically, the process of dropping the diiodomethane whose surface tension is known thereon and obtaining the contact angle thereof is repeated five times to obtain an average value of the obtained five contact angle values. Then, the surface energy can be obtained by substituting the value (Strom value) regarding the solvent surface tension by the Owens-Wendt-Rabel-Kaelble method using the obtained average values of the contact angles for the deionized water and diiodomethane. The numerical value of the surface energy for each polymer segment of the block copolymer can be obtained for a homopolymer made of only the monomer forming the polymer segment by the above-described method.

When the block copolymer comprises the above-described side chain, the polymer segment comprising the side chain may have a higher surface energy than the other polymer segment. For example, if the polymer segment A of the block copolymer comprises the side chain, the polymer segment A may have a higher surface energy than the polymer segment B. In this case, the surface energy of the polymer segment A may be in a range of about 20 mN/m to 40 mN/m. The surface energy of the polymer segment A may be 22 mN/m or more, 24 mN/m or more, 26 mN/m or more, or 28 mN/m or more. The surface energy of the polymer segment A may be 38 mN/m or less, 36 mN/m or less, 34 mN/m or less, or 32 mN/m or less. The block copolymer comprising such a polymer segment A and exhibiting a difference in surface energy from the polymer segment B as above can exhibit excellent self-assembly properties.

E. Condition 5

The absolute value of the difference in density between the polymer segment A and the polymer segment B in the block copolymer may be 0.25 g/cm³ or more, 0.3 g/cm³ or more, 0.35 g/cm³ or more, 0.4 g/cm³ or more, or 0.45 g/cm³ or more. The absolute value of the difference in density may be 0.9 g/cm³ or less, 0.8 g/cm³ or less, 0.7 g/cm³ or less, 0.65 g/cm³ or less, or 0.6 g/cm³ or less. The structure in which the polymer segment A and the polymer segment B having the absolute value of the density difference in this range are linked by covalent bonds can induce effective microphase separation by phase separation due to proper non-compatibility.

The density of each polymer segment in the block copolymer can be measured using a known buoyancy method, and for example, the density can be measured by analyzing the mass of the block copolymer in a solvent, such as ethanol, which is known in mass and density in air.

When the above-described side chain is included, the polymer segment comprising the side chain may have a lower density than the other polymer segment. For example, if the polymer segment A of the block copolymer comprises the side chain, the polymer segment A may have a lower density than the polymer segment B. In this case, the density of the polymer segment A may be in a range of about 0.9 g/cm³ to 1.5 g/cm³ or so. The density of the polymer segment A may be 0.95 g/cm³ or more. The density of the polymer segment A may be 1.4 g/cm³ or less, 1.3 g/cm³ or less, 1.2 g/cm³ or less, 1.1 g/cm³ or less, or 1.05 g/cm³ or less. The block copolymer comprising such a polymer segment A and exhibiting a density difference with the polymer segment B as above can exhibit excellent self-assembly properties.

As described above, the block copolymer may satisfy any one of the above conditions, or may satisfy two or more selected from them.

In one example, the block copolymer may comprise a polymer segment A satisfying any one or two or more of Conditions 1 to 3 among the above conditions and a polymer segment B having a difference in surface energy according to Condition 4 above.

Although not limited by theory, the polymer segment A satisfying any one of Conditions 1 to 3 can exhibit crystallinity or liquid crystallinity, and accordingly, it can be packed with regularity upon forming the self-assembled structure. In this state, when the polymer segment A and the polymer segment B satisfy the difference in surface energy according to Condition 4, the domains formed by the respective polymer segments A and B are substantially neutralized, whereby it can be oriented vertically in the structure of the above-mentioned laminate.

In the block copolymer, the volume fraction of the polymer segment A may be in a range of 0.4 to 0.8, and the volume fraction of the polymer segment B may be in a range of 0.2 to 0.6. The sum of the volume fractions of the polymer segments A and B may be 1. The block copolymer comprising each of the above-mentioned segments at the above volume fractions may exhibit excellent self-assembly properties in the laminate. The volume fraction of each block in the block copolymer can be determined based on the density and the molecular weight measured by GPC (gel permeation chromatography), of each block.

As other conditions, the block copolymer may have a number average molecular weight (Mn) in a range of, for example, 3,000 to 300,000. In this specification, the term number average molecular weight is a converted value for standard polystyrene measured using GPC (gel permeation chromatograph), and the term molecular weight herein means a number average molecular weight, unless otherwise specified. In another example, the molecular weight (Mn) may be, for example, 3000 or more, 5000 or more, 7000 or more, 9000 or more, 11000 or more, 13000 or more, or 15000 or more. In another example, the molecular weight (Mn) may be 250000 or less, 200000 or less, 180000 or less, 160000 or less, 140000 or less, 120000 or less, 90000 or less, 80000 or less, 70000 or less, 60,000 or less, 50000 or less, 40000 or less, 30000 or less, or 25000 or less. The block copolymer may have a polydispersity (Mw/Mn) in a range of 1.01 to 1.60. In another example, the polydispersity may be about 1.1 or more, about 1.2 or more, about 1.3 or more, or about 1.4 or more.

In this range, the block copolymer may exhibit proper self-assembly properties in the laminate. The number average molecular weight of the block copolymer or the like can be adjusted in consideration of the desired self-assembled structure and the like.

The above-mentioned conditions can be achieved, for example, by controlling the structure of the block copolymer. For example, the polymer segment A of the block copolymer satisfying one or more of the above-mentioned conditions may comprise the side chain to be described below. The polymer segment A may comprise a ring structure, where the side chain may be substituted on the ring structure. The side chain may be directly substituted on the ring structure or may be substituted via a suitable linker. The ring structure may be an aromatic structure or an alicyclic ring structure as described above. No halogen atom may be present in such a ring structure. The polymer segment B contained in the block copolymer together with the polymer segment A may comprise 3 or more halogen atoms. At this time, the polymer segment B may comprise a ring structure, where the halogen atoms may be substituted on the ring structure. The ring structure may be an alicyclic ring structure or an aromatic structure as described above.

Here, the aromatic structure or the alicyclic ring structure may be a structure contained in the main chain of the polymer segment, or may be a structure linked to the polymer segment main chain in a side chain form.

In one example, the block copolymer satisfying one or more of the above conditions may comprise a polymer segment A comprising a side chain and a polymer segment B different therefrom. Here, the side chain may be a side chain having 8 or more chain-forming atoms, as described below. The polymer segment A may be a polymer segment satisfying any one of the above-described conditions 1 to 3, satisfying two or more of the foregoing, or satisfying all of the above conditions.

Here, the term side chain means a chain connected to the main chain of the polymer, and the term chain-forming atom is an atom forming the side chain, which means an atom forming the straight chain structure of the chain. The side chain may be linear or branched, but the number of chain-forming atoms is calculated by only the number of atoms forming the longest straight chain, where other atoms bonded to the chain-forming atoms (for example, when the chain-forming atom is a carbon atom, hydrogen atoms bonding to the carbon atom, etc.) are not included in the calculation. For example, in the case of a side chain, the number of chain-forming atoms can be calculated as the number of chain-forming atoms forming the longest chain moiety. For example, when the side chain is an n-pentyl group, all of the chain-forming atoms are carbon atoms and the number thereof is 5, and even when the side chain is a 2-methylpentyl group, all of the chain-forming atoms are carbon atoms and the number thereof is 5. The chain-forming atom may be exemplified by carbon, oxygen, sulfur or nitrogen, and the like, and the appropriate chain-forming atom may be carbon, oxygen or nitrogen, or may be carbon or oxygen. The number of chain-forming atoms may be 8 or more, 9 or more, 10 or more, 11 or more, or 12 or more. The number of the chain-forming atoms may be 30 or less, 25 or less, 20 or less, or 16 or less.

For the control of the above-described conditions, the polymer segment A of the block copolymer may have a chain with 8 or more chain-forming atoms connected to the side chain. In this specification, the term chain and side chain may refer to the object identical to each other.

The side chain may be a chain comprising 8 or more, 9 or more, 10 or more, 11 or more, or 12 or more chain-forming atoms, as mentioned above. Also, the number of the chain-forming atoms may be 30 or less, 25 or less, 20 or less, or 16 or less. The chain-forming atom may be a carbon, oxygen, nitrogen or sulfur atom and may suitably be carbon or oxygen.

As the side chain, a hydrocarbon chain such as an alkyl group, an alkenyl group or an alkynyl group can be exemplified. At least one of the carbon atoms of the hydrocarbon chain may be replaced by a sulfur atom, an oxygen atom or a nitrogen atom.

When the side chain is connected to the ring structure, the chain may be directly connected to the ring structure or may be connected via a linker. The linker may be exemplified by an oxygen atom, a sulfur atom, —NR₁—, —S(═O)₂—, a carbonyl group, an alkylene group, an alkenylene group, an alkynylene group, —C(═O)—X₁— or —X₁—C(═O)—. Here, R₁ may be hydrogen, an alkyl group, an alkenyl group, an alkynyl group, an alkoxy group or an aryl group, and X₁ may be a single bond, an oxygen atom, a sulfur atom, —NR₂—, —S(═O)₂—, an alkylene group, an alkenylene group or an alkynylene group, where R₂ may be hydrogen, an alkyl group, an alkenyl group, an alkynyl group, an alkoxy group or an aryl group. The suitable linker may be exemplified by an oxygen atom. The side chain may be connected to a ring structure such as an aromatic structure, for example, via an oxygen atom or a nitrogen atom.

When the ring structure such as the aromatic structure described above is connected to the main chain of the polymer segment in a side chain form, the aromatic structure may also be directly connected to the main chain or may be connected via a linker. In this case, the linker can be exemplified by an oxygen atom, a sulfur atom, —S(═O)₂—, a carbonyl group, an alkylene group, an alkenylene group, an alkynylene group, —C(═O)—X₁— or —X₁—C(═O)—, where X₁ may be a single bond, an oxygen atom, a sulfur atom, —S(═O)₂—, an alkylene group, an alkenylene group or an alkynylene group. The suitable linker connecting the aromatic structure to the main chain can be exemplified by —C(═O)—O— or —O—C(═O)—, but is not limited thereto.

In another example, the ring structure such as the aromatic structure contained in the polymer segment B of the block copolymer may comprise 1 or more, 2 or more, 3 or more, 4 or more, or 5 or more halogen atoms. The number of halogen atoms may be, for example, 30 or less, 25 or less, 20 or less, 15 or less, or 10 or less. The halogen atom may be exemplified by fluorine or chlorine, and the like, and the use of a fluorine atom may be advantageous. As described above, the polymer segment having a ring structure such as an aromatic structure containing a halogen atom can efficiently realize a phase separation structure through proper interaction with other polymer segments.

Here, the polymer segment A may be, for example, a polymer segment comprising a unit represented by Formula 1 below. The polymer segment may be a polymer segment containing a unit of Formula 1 below as a main component. In this specification, the fact that any polymer segment comprises a certain unit as a main component may mean a case where the polymer segment comprises the unit 60% or more, 70% or more, 80% or more, 90% or more, or 95% or more by weight, or a case where it comprises the unit 60 mol % or more, 70 mol % or more, 80 mol % or more, 90 mol % or more, or 95 mol % or more.

In Formula 1, R is hydrogen or an alkyl group having 1 to 4 carbon atoms, X is a single bond, an oxygen atom, a sulfur atom, —S(═O)₂—, a carbonyl group, an alkylene group, an alkenylene group, an alkynylene group, —C(═O)—X₁— or —X₁—C(═O)—, where X₁ is an oxygen atom, a sulfur atom, —S(═O)₂—, an alkylene group, an alkenylene group or an alkynylene group, and Y is a monovalent substituent comprising a ring structure to which the side chain having 8 or more chain-forming atoms is linked.

When the side chain is an alkyl group, the alkyl group may contain 8 or more, 9 or more, 10 or more, 11 or more, or 12 or more carbon atoms, where the number of carbon atoms of this alkyl group may be 30 or less, 25 or less, 20 or less, or 16 or less. Also, when the side chain is an alkenyl group or alkynyl group, it may contain 8 or more, 9 or more, 10 or more, 11 or more, or 12 or more carbon atoms, where the number of carbon atoms of this alkenyl group or alkynyl group may be 30 or less, 25 or less, 20 or less, or 16 or less.

In another example, X of Formula 1 may be —C(═O)O— or —OC(═O)—.

In Formula 1, Y is a substituent comprising the above-described side chain, which may be, for example, a substituent containing an aromatic structure having 6 to 18 carbon atoms or 6 to 12 carbon atoms. Here, the chain may be, for example, a linear alkyl group containing 8 or more, 9 or more, 10 or more, 11 or more, or 12 or more carbon atoms. This alkyl group may contain 30 or less, 25 or less, 20 or less, or 16 or less carbon atoms. Such a chain may be linked to the aromatic structure directly or via the above-mentioned linker.

In another example, the unit of Formula 1 above in the polymer segment A may be a unit of Formula 2 below.

In Formula 2, R is hydrogen or an alkyl group having 1 to 4 carbon atoms, X is —C(═O)—O—, P is an arylene group having 6 to 12 carbon atoms, Q is an oxygen atom, and Z is the side chain having 8 or more chain-forming atoms.

In another example, P in Formula 2 may be phenylene, and in another example, Z may be a linear alkyl group having 9 to 20 carbon atoms, 9 to 18 carbon atoms, 9 to 16 carbon atoms, 10 to 16 carbon atoms, 11 to 16 carbon atoms or 12 to 16 carbon atoms. Here, when P is phenylene, Q may be connected to the para position of the phenylene. Here, the alkyl group, arylene group, phenylene group and side chain may be optionally substituted with one or more substituents.

The polymer segment B of the block copolymer may be, for example, a polymer segment containing a unit represented by Formula 3 below. The polymer segment may comprise a unit of Formula 3 below as a main component.

In Formula 3, X₂ is a single bond, an oxygen atom, a sulfur atom, —S(═O)₂—, an alkylene group, an alkenylene group, an alkynylene group, —C(═O)—X₁— or —X₁—C(═O)—, where X₁ is a single bond, an oxygen atom, a sulfur atom, —S(═O)₂—, an alkylene group, an alkenylene group or an alkynylene group, and W is an aryl group containing at least one halogen atom.

In another example, X₂ of Formula 3 may be a single bond or an alkylene group.

In Formula 3, the aryl group of W may be an aryl group having 6 to 12 carbon atoms or a phenyl group, and this aryl group or phenyl group may contain 1 or more, 2 or more, 3 or more, 4 or more, or 5 or more halogen atoms. Here, the number of halogen atoms may be, for example, 30 or less, 25 or less, 20 or less, 15 or less, or 10 or less. As the halogen atom, a fluorine atom may be exemplified.

In another example, the unit of Formula 3 may be represented by Formula 4 below.

In Formula 4, X₂ is a single bond, an oxygen atom, a sulfur atom, —S(═O)₂—, an alkylene group, an alkenylene group, an alkynylene group, —C(═O)—X₁— or —X₁—C(═O)—, where X₁ is a single bond, an oxygen atom, a sulfur atom, —S(═O)₂—, an alkylene group, an alkenylene group or an alkynylene group, R₁ to R₅ are each independently hydrogen, an alkyl group, a haloalkyl group or a halogen atom, and the number of halogen atoms contained in R₁ to R₅ is 1 or more.

In Formula 4, R₁ to R₅ may be each independently a hydrogen atom, an alkyl group having 1 to 4 carbon atoms or a haloalkyl group having 1 to 4 carbon atoms or halogen, where halogen may be chlorine or fluorine.

In Formula 4, 2 or more, 3 or more, 4 or more, 5 or more, or 6 or more halogens may be included in R₁ to R₅ may contain halogen. The upper limit of the halogen number is not particularly limited and may be, for example, 12 or less, 8 or less, or 7 or less.

As described above, the block copolymer may be a diblock copolymer comprising any two of the above units, or may be a block copolymer comprising any one or both of the two polymer segments together with other polymer segments.

The method of producing such a block copolymer is not particularly limited. The block copolymer may be polymerized by, for example, an LRP (Living Radical Polymerization) method, and an example thereof includes anionic polymerization in which the block copolymer is synthesized in the presence of an inorganic acid salt such as an alkali metal or an alkali earth metal by using an organic rare earth metal complex as a polymerization initiator or by using an organic alkali metal compound as a polymerization initiator, an anionic polymerization method in which the block copolymer is synthesized in the presence of an organic aluminum compound by using an organic alkali metal compound as a polymerization initiator, an atom transfer radical polymerization method (ATRP) using an atom transfer radical polymerization agent as a polymerization inhibitor, an ARGET (Activators Regenerated by Electron Transfer) atom transfer radical polymerization method (ATRP), which uses an atom transfer radical polymerization agent as a polymerization initiator, but performs polymerization under an organic or inorganic reducing agent that generates electrons, an ICAR (Initiators for Continuous Activator Regeneration) atom transfer radical polymerization method (ATRP), a polymerization method by reversible addition-fragmentation chain transfer (RAFT) using an inorganic reducing agent and a reversible addition-fragmentation chain transfer agent or a method of using an organotellurium compound as an initiator, and the like, and a suitable method may be selected among these methods and applied.

For example, the block copolymer can be prepared in a manner comprising polymerizing a reactant comprising monomers capable of forming the polymer segments in the presence of a radical initiator and a living radical polymerization reagent by a living radical polymerization method. The process of producing the polymer segment copolymer may further comprise, for example, a process of precipitating the polymerization product produced through the above processes in a non-solvent.

The kind of the radical initiator is not particularly limited, which may be appropriately selected in consideration of polymerization efficiency, and for example, an azo compound such as AIBN (azobisisobutyronitrile) or 2,2′-azobis-(2,4-dimethylvaleronitrile), or peroxide series such as BPO (benzoyl peroxide) or DTBP (di-t-butyl peroxide) may be used.

The living radical polymerization process may be performed in a solvent such as, for example, methylene chloride, 1,2-dichloroethane, chlorobenzene, dichlorobenzene, benzene, toluene, acetone, chloroform, tetrahydrofuran, dioxane, monoglyme, diglyme, dimethylformamide, dimethyl sulfoxide or dimethylacetamide.

As the non-solvent, an alcohol such as methanol, ethanol, normal propanol or isopropanol, a glycol such as ethylene glycol, n-hexane, cyclohexane, n-heptane or ether series such as petroleum ether can be used, without being limited thereto.

The present inventors have found that a self-assembled structure can be effectively formed by putting deviation between the upper temperature and the lower temperature of the polymer film in the process of annealing the polymer film to form a self-assembled structure.

Accordingly, the production method of the present application comprises a step of forming a self-assembled structure of the block copolymer in the polymer film comprising the block copolymer, wherein it comprises a step of annealing the polymer film in such a state that in the step the difference (T1−T2) between the temperature (T1) of one side of the polymer film, for example, the upper temperature and the temperature (T2) of the other side of the polymer film, for example, the lower temperature is in a range of 40° C. to 500° C. The temperature of the other side of the polymer film may be the substrate side temperature.

In another example, the temperature difference (T1−T2) may be about 50° C. or higher, 60° C. or higher, 70° C. or higher, 80° C. or higher, 90° C. or higher, 100° C. or higher, 110° C. or higher, 120° C. or higher, 130° C. or higher, or 150° C. or higher, and may be 490° C. or lower, 480° C. or lower, 470° C. or lower, 460° C. or lower, 450° C. or lower, 440° C. or lower, 430° C. or lower, 420° C. or lower, 410° C. or lower, or 400° C. or lower, 390° C. or lower, or 380° C. or lower.

In the above process, the temperature (T1) of one side of the polymer film, for example, the upper temperature may be maintained within a range of about 100° C. to 300° C. In addition, the temperature (T2) of the other side of the polymer film, for example, the temperature of the lower side may be maintained within a range of about −200° C. to 100° C.

For example, the temperature deviation can be maintained by performing annealing in a state where an appropriate heat source or heat sink is placed on the upper and/or lower portions of the polymer film applied for annealing. Here, preferably, the heat applied to the polymer film is applied as uniformly as possible, and it may be appropriate that it is applied thereto in a static state without movement of the polymer film.

This annealing can be performed, for example, in a vacuum or normal pressure state.

The time for which this annealing is performed is not particularly limited, and can be performed within a range of, for example, about 1 minute to 72 hours, but this can be changed as needed. If necessary, the annealing may also be performed in a suitable non-polar solvent and/or polar solvent.

The present application also relates to a method for producing a patterned substrate. The production method may comprise a step of forming a polymer film on a substrate, for example, a substrate to be patterned by the above method.

For example, the block copolymer or the coating liquid comprising the same may be coated on the substrate and annealed by the above-described method to induce a self-assembled structure. At this time, the polymer film can be formed in direct contact with the substrate. That is, according to the method of the present application, in order to achieve the vertical orientation of the block copolymer, it is possible to effectively form a self-assembled structure even in a state where the so-called neutralization treatment being known is not performed.

Here, the type of the substrate is not particularly limited. This substrate may be etched via a mask formed by the block copolymer film in the method for producing a patterned substrate. As such a substrate, for example, various types of substrates requiring formation of a pattern on the surface may all be used. This type of substrate may include, for example, a silicon substrate, a silicon germanium substrate, a GaAs substrate, a silicon oxide substrate, and the like. As the substrate, for example, a substrate applied to formation of finFETs (fin field effect transistors) or other electronic devices such as diodes, transistors or capacitors may be used. In addition, other materials such as ceramics may be used as the substrate depending on the application, and the types of substrates that can be applied in the present application are not limited thereto.

The method for producing a patterned substrate may further perform a step of selectively removing any one polymer segment of the block copolymer in the polymer film comprising the block copolymer in which the self-assembly structure is formed as above.

For example, it may comprise a process of selectively removing the polymer segment A or B of the block copolymer in the laminate. The production method may comprise selectively removing one or more polymer segments of the block copolymer, and then etching the substrate using the polymer film as a mask. In this way, it is possible to form, for example, a nanoscale fine pattern. In addition, various types of patterns such as nano-rods or nano-holes can be formed through the above-described method depending on the shape of the block copolymer in the polymer film. If necessary, a copolymer different from the block copolymer or a homopolymer, and the like may be mixed for pattern formation.

The method of selectively removing any one polymer segment of the block copolymer in the above method is not particularly limited, and for example, a method of removing a relatively soft polymer segment by irradiating the polymer film with an appropriate electromagnetic wave, for example, ultraviolet or the like, can be used. In this case, the ultraviolet irradiation condition is determined according to the type of the polymer segment of the block copolymer, and the method can be performed, for example, by being irradiated with ultraviolet having a wavelength of about 254 nm for 1 minute to 60 minutes.

Following the ultraviolet irradiation, a step of treating the polymer film with an acid or the like to further remove the segment decomposed by ultraviolet may also be performed.

The step of etching the substrate using the polymer film in which the polymer segments are selectively removed as a mask is not particularly limited, which may be performed, for example, through a reactive ion etching step using CF₄/Ar ions or the like and following this process, a step of removing the polymer film from the substrate by an oxygen plasma treatment or the like may also be performed.

Advantageous Effects

The present application is a production method capable of effectively forming on a substrate a polymer film comprising highly aligned block copolymers without orientation defects, coordination number defects, distance defects, and the like, which can provide a method for producing a polymer film capable of being effectively applied to production of various patterned substrates and a method for producing a patterned substrate using the same.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a view showing an analysis result of GISAXS for the polymer film of Example 1.

FIGS. 2 and 3 are SEM images of the self-assembled polymer patterns of Examples 1 and 2, respectively.

MODE FOR INVENTION

Hereinafter, the present application will be described in detail by way of examples according to the present application and comparative examples, but the scope of the present application is not limited by the following examples.

1. NMR Measurement

NMR analyses were performed at room temperature using an NMR spectrometer including a Varian Unity Inova (500 MHz) spectrometer with a triple resonance 5 mm probe. The analytes were diluted in a solvent for NMR measurement (CDCl₃) to a concentration of about 10 mg/ml, and chemical shifts were expressed in ppm.

<Application Abbreviation>

br=broad signal, s=singlet, d=doublet, dd=double doublet, t=triplet, dt=double triplet, q=quartet, p=quintet, m=multiplet.

2. GPC (Gel Permeation Chromatograph)

The number average molecular weight (Mn) and the molecular weight distribution were measured using GPC (gel permeation chromatography). Into a 5 mL vial, an analyte such as block copolymers of Examples or Comparative Examples or a giant initiator is put and diluted in THF (tetrahydrofuran) to be a concentration of about 1 mg/mL or so. Then, a standard sample for calibration and a sample to be analyzed were filtered through a syringe filter (pore size: 0.45 μm) and then measured. As the analytical program, ChemStation from Agilent Technologies was used, and the elution time of the sample was compared with the calibration curve to obtain the weight average molecular weight (Mw) and the number average molecular weight (Mn), respectively, and the molecular weight distribution (PDI) was calculated by the ratio (Mw/Mn) thereof. The measurement conditions of GPC are as follows.

<GPC Measurement Condition>

Instrument: 1200 series from Agilent Technologies

Column: using two PLgel mixed B from Polymer Laboratories

Solvent: THF

Column temperature: 35° C.

Sample concentration: 1 mg/mL, 200 μL injection

Standard sample: polystyrene (Mp: 3900000, 723000, 316500, 52200, 31400, 7200, 3940, 485)

3. GISAXS (Grazing Incidence Small Angle X-Ray Scattering)

The grazing incidence small angle X-ray scattering (GISAXS) analysis was performed using a Pohang accelerator 3C beamline. The block copolymer to be analyzed was diluted in fluorobenzene to a solid concentration of about 0.7 weight % to prepare a coating liquid, and the coating liquid was spin-coated on a base material to a thickness of about 5 nm. The coating area was adjusted to 2.25 cm² or so (width: 1.5 cm, height: 1.5 cm). The coated polymer film was dried at room temperature for about 1 hour and thermally annealed again at about 160° C. for about 1 hour to induce a phase separation structure. Subsequently, a film, in which the phase separation structure was formed, was formed. After an X-ray was incident on the film at an incident angle in a range of about 0.12 degrees to 0.23 degrees corresponding to the angle between the critical angle of the film and the critical angle of the base material, an X-ray diffraction pattern, which was scattered from the film to a detector (2D marCCD) and exited, was obtained. At this time, the distance from the film to the detector was selected as such a range that the self-assembly pattern formed on the film was well observed within a range of about 2 m to 3 m. As the base material, a base material having a hydrophilic surface (a silicon substrate treated with a piranha solution and having a room temperature wetting angle of about 5 degrees to pure water) or a base material having a hydrophobic surface (a silicon substrate treated with HMDS (hexamethyldisilazane) and having a room temperature wetting angle of about 60 degrees to pure water) was used.

4. XRD Analysis Method

The XRD analysis was performed by transmitting X rays to a sample at a Pohang accelerator 4C beamline to measure the scattering intensity according to the scattering vector (q). As the sample, a polymer in a powder state dried by purifying a synthesized polymer without special pretreatment and then maintaining it in a vacuum oven for one day or so, was placed in a cell for XRD measurement and used. Upon the XRD pattern analysis, an X-ray with a vertical size of 0.023 mm and a horizontal size of 0.3 mm was used and a 2D marCCD was used as a detector. A 2D diffraction pattern scattered and exited was obtained as an image. The obtained diffraction pattern was analyzed by a numerical analytical method to which a least-square method was applied to obtain information such as a scattering vector and a half-value width. Upon the analysis, an origin program was applied, and the profile of the XRD patterns was subjected to Gaussian fitting in a state where a portion showing the smallest intensity in the XRD diffraction patterns was taken as a baseline and the intensity in the above was set to zero, and then the scattering vector and the half-value width were obtained from the fitted results.

5. Measurement of Surface Energy

The surface energy was measured using a drop shape analyzer (DSA100 product from KRUSS). A coating liquid was prepared by diluting the substance (polymer), which is measured, in fluorobenzene to a solid concentration of about 2 weight %, and the prepared coating liquid was spin-coated on a silicon wafer to a thickness of about 50 nm and a coating area of 4 cm² (width: 2 cm, height: 2 cm). The coating layer was dried at room temperature for about 1 hour and then subjected to thermal annealing at about 160° C. for about 1 hour. The process of dropping the deionized water whose surface tension was known on the film subjected to thermal annealing and obtaining the contact angle thereof was repeated five times to obtain an average value of the obtained five contact angle values. In the same manner, the process of dropping the diiodomethane whose surface tension was known thereon and obtaining the contact angle thereof was repeated five times to obtain an average value of the obtained five contact angle values. The surface energy was obtained by substituting the value (Strom value) regarding the solvent surface tension by the Owens-Wendt-Rabel-Kaelble method using the obtained average values of the contact angles for the deionized water and diiodomethane. The numerical value of the surface energy for each polymer segment of the block copolymer was obtained for a homopolymer made of only the monomer forming the polymer segment by the above-described method.

6. GIWAXS (Grazing Incidence Wide Angle X-Ray Scattering)

The grazing incidence wide angle X-ray scattering (GIWAXS) analysis was performed using a Pohang accelerator 3C beamline. The homopolymer to be analyzed was diluted in toluene to a solid concentration of about 1 weight % to prepare a coating liquid, and the coating liquid was spin-coated on a base material to a thickness of about 30 nm. The coating area was adjusted to about 2.25 cm² (width: 1.5 cm, height: 1.5 cm). The coated polymer film was dried at room temperature for about 1 hour and then subjected to thermal annealing at a temperature of about 160° C. for about 1 hour to form a film. After an X-ray was incident on the film at an incident angle in a range of about 0.12 degrees to 0.23 degrees corresponding to the angle between the critical angle of the film and the critical angle of the base material, an X-ray diffraction pattern, which was scattered from the film to a detector (2D marCCD) and exited, was obtained. At this time, the distance from the film to the detector was selected as such a range that the crystal or liquid crystal structure formed on the film was well observed within a range of about 0.1 m to 0.5 m. As the base material, a silicon substrate treated with a piranha solution and having a room temperature wetting angle of about 5 degrees to pure water was used. In the GIWAXS spectrum, the scattering intensity in the azimuthal angle range of −90 degrees to 90 degrees of the diffraction pattern in the range of 12 nm⁻¹ to 16 nm⁻¹ (azimuthal angle when the upward direction of the diffraction pattern (out-of-plane diffraction pattern) is set as 0 degrees) was plotted, and the half-value width was obtained from the graph through Gauss fitting. Furthermore, when half of the peak was observed upon Gauss fitting, twice the value of the obtained half-value width (FWHM) was defined as the half-value width of the peak.

7. DSC Analysis

The DSC analysis was performed using PerkinElmer DSC800 equipment. Using the equipment, it was performed by a method in which the sample to be analyzed was heated at a speed of 10° C. per minute from 25° C. to 200° C., cooled again at a speed of −10° C. per minute from 200° C. to −80° C., and raised at a speed of 10° C. per minute from −80° C. to 200° C. under a nitrogen atmosphere to obtain an endothermic curve. The obtained endothermic curve was analyzed to obtain a temperature (melting transition temperature, Tm) indicating a melting transition peak or a temperature (isotropic transition temperature, Ti) indicating an isotropic transition peak, and the area of the peak was obtained. Here, the temperature was defined as the temperature corresponding to the apex of each peak. The area per unit mass of each peak is defined as the value obtained by dividing the area of each peak by the mass of the sample, and this calculation can be calculated using the program provided by the DSC equipment.

Preparation Example 1. Synthesis of Monomer (A)

A monomer (DPM-C12) of Formula A below was synthesized in the following manner. Hydroquinone (10.0 g, 94.2 mmol) and 1-bromododecane (23.5 g, 94.2 mmol) were placed in a 250 mL flask, dissolved in 100 mL of acetonitrile, and then an excess amount of potassium carbonate was added thereto and reacted at 75° C. for about 48 hours under a nitrogen condition. After the reaction, the remaining potassium carbonate was filtered off and the acetonitrile used in the reaction was also removed. A mixed solvent of DCM (dichloromethane) and water was added thereto to work up the mixture, and the separated organic layers were collected and passed through MgSO₄ to be dehydrated. Subsequently, the target product (4-dodecyloxyphenol) (9.8 g, 35.2 mmol) in a white solid phase was obtained in a yield of about 37% using dichloromethane in column chromatography.

<NMR Analysis Result>

¹H-NMR (CDCl₃): d6.77 (dd, 4H); δd4.45 (s, 1H); d3.89 (t, 2H); d1.75 (p, 2H); d1.43 (p, 2H); d1.33-1.26 (m, 16H); d0.88 (t, 3H).

The synthesized 4-docecyloxyphenol (9.8 g, 35.2 mmol), methacrylic acid (6.0 g, 69.7 mmol), DCC (dicyclohexylcarbodiimide) (10.8 g, 52.3 mmol) and DMAP (p-dimethylaminopyridine) (1.7 g, 13.9 mmol) were placed in the flask and 120 mL of methylene chloride was added thereto, and then reacted at room temperature for 24 hours under nitrogen. After completion of the reaction, the salt (urea salt) generated during the reaction was filtered off and the remaining methylene chloride was also removed. Impurities were removed using hexane and DCM (dichloromethane) as the mobile phase in column chromatography and the product obtained again was recrystallized in a mixed solvent of methanol and water (1:1 mix) to obtain the target product (7.7 g, 22.2 mmol) in a white solid phase in a yield of 63%.

<NMR Analysis Result>

¹H-NMR (CDCl₃): d7.02 (dd, 2H); δd6.89 (dd, 2H); d6.32 (dt, 1H); d5.73 (dt, 1H); d3.94 (t, 2H); δd 2.05 (dd, 3H); d1.76 (p, 2H); δd1.43 (p, 2H); 1.34-1.27 (m, 16H); d0.88 (t, 3H).

In Formula A, R is a linear alkyl group having 12 carbon atoms.

XRD and DSC Analyses

A homopolymer was prepared using the monomer (A) of Preparation Example 1, and GIWAXS and DSC were analyzed for the prepared homopolymer. Here, the homopolymer was prepared by a method of synthesizing a macromonomer using the monomer (A) in the following examples. As a result of the DSC analysis for the homopolymer, the corresponding polymer showed a melting transition temperature of about −3° C. and an isotropic transition temperature of about 15° C. Also, the ratio (M/I) of the area (M) of the melting transition peak to the area (I) of the isotropic transition peak in the DSC analysis of the homopolymer was about 3.67, the half-value width of the peak in an azimuthal angle of −90 degrees to −70 degrees of the diffraction pattern of the scattering vector in a range of 12 nm⁻¹ to 16 nm⁻¹ in GIWAXS was about 48 degrees, and the half-value width of the peak in an azimuthal angle of 70 degrees to 90 degrees of the diffraction pattern of the scattering vector in a range of 12 nm⁻¹ to 16 nm⁻¹ in GIWAXS was about 58 degrees. Furthermore, in the X-ray diffraction analysis (XRD), a peak having a half-value width of about 0.57 nm⁻¹ or so was observed at a scattering vector value of 1.96 nm⁻¹.

Preparation Example 2. Synthesis of Block Copolymer (A)

2.0 g of the monomer (A) of Preparation Example 1, 64 mg of cyanoisoproyl dithiobenzoate as an RAFT (reversible addition-fragmentation chain transfer) reagent, 23 mg of AIBN (azobisisobutyronitrile) as a radical initiator and 5.34 mL of benzene were placed in a 10 mL Schlenk flask and stirred at room temperature for 30 minutes under a nitrogen atmosphere, and then an RAFT (reversible addition-fragmentation chain transfer) polymerization reaction was performed at 70° C. for 4 hours. After the polymerization, the reaction solution was precipitated in 250 mL of methanol as an extraction solvent, and then filtered under reduced pressure and dried to prepare a pink macro initiator. 0.3 g of the macro initiator, 2.7174 g of a pentafluorostyrene monomer and 1.306 mL of benzene were placed in a 10 mL Schlenk flask and stirred at room temperature for 30 minutes under a nitrogen atmosphere, and then an RAFT (reversible addition-fragmentation chain transfer) polymerization reaction was performed at 115° C. for 4 hours. After the polymerization, the reaction solution was precipitated in 250 mL of methanol as an extraction solvent, and then filtered under reduced pressure and dried to prepare a pale pink polymer segment copolymer. The yield of the block copolymer was about 18 weight %, and the number average molecular weight (Mn) and the molecular weight distribution (Mw/Mn) were 39,400 and 1.18, respectively. The block copolymer comprises a polymer segment A, which is derived from the monomer (A) of Preparation Example 1 and has 12 chain-forming atoms (the number of carbon atoms of R in Formula A), and a polymer segment B derived from the pentafluorostyrene monomer. Here, the volume fraction of the polymer segment A was about 0.47, and the volume fraction of the polymer segment B was about 0.53. The surface energy and density of the polymer segment A of the block copolymer were 30.83 mN/m and 1 g/cm³, respectively, and the surface energy and density of the polymer segment B were 24.4 mN/m and 1.57 g/cm³, respectively. Also, the result obtained by substituting the number of chain-forming atoms (12) in the polymer segment A of the block copolymer and the scattering vector value (q) in which the peak having the largest peak area was identified in the scattering vector range of 0.5 nm⁻¹ to 10 nm⁻¹ upon the X-ray diffraction analysis into the equation nq/(2×π), respectively, was about 3.75.

Preparation Example 3. Synthesis of Block Copolymer (B)

A block copolymer, in which a number average molecular weight (Mn) and a molecular weight distribution (Mw/Mn) were 17,800 and 1.14, respectively, was prepared by synthesizing it in the same manner as in Preparation Example 2 but controlling the ratio of the monomers and the polymerization conditions, and the like. The block copolymer comprises a polymer segment A, which is derived from the monomer (A) of Preparation Example 1 and has 12 chain-forming atoms (the number of carbon atoms of R in Formula A), and a polymer segment B derived from the pentafluorostyrene monomer. Here, the volume fraction of the polymer segment A was about 0.69, and the volume fraction of the polymer segment B was about 0.31. The surface energy and density of the polymer segment A of the block copolymer were 30.83 mN/m and 1 g/cm³, respectively, and the surface energy and density of the polymer segment B were 24.4 mN/m and 1.57 g/cm³, respectively. Also, the result obtained by substituting the number of chain-forming atoms (12) in the polymer segment A of the block copolymer and the scattering vector value (q) in which the peak having the largest peak area was identified in the scattering vector range of 0.5 nm⁻¹ to 10 nm⁻¹ upon the X-ray diffraction analysis into the equation nq/(2×π), respectively, was about 3.75.

Example 1

A polymer film was formed on a silicon wafer substrate using the block copolymer (A) of Preparation Example 2. Specifically, a coating liquid prepared by diluting the block copolymer in fluorobenzene to a solid concentration of about 1.2 weight % was spin-coated on the substrate to a thickness of about 50 nm and dried at room temperature for about 1 hour. Subsequently, the temperature of the upper side of the polymer film was set at a temperature of about 180° C., the temperature of the lower side was maintained at about −195° C., and the film was annealed for about 180 seconds to form a self-assembled film. For the formed film, GISAXS analysis and SEM (scanning electron microscope) image capture were performed. FIG. 1 is a GISAXS analysis result for the polymer film, and FIG. 2 is an SEM image of the self-assembled film. It can be confirmed that the self-assembled film has formed a vertically oriented lamellar phase.

Example 2

A polymer film was formed on a silicon wafer substrate using the block copolymer (B) of Preparation Example 3. Specifically, a coating liquid prepared by diluting the block copolymer in fluorobenzene to a solid concentration of about 0.7 weight % was spin-coated on the substrate to a thickness of about 35 nm and dried at room temperature for about 1 hour. Subsequently, the temperature of the upper side of the polymer film was set at a temperature of about 240° C., the temperature of the lower side was maintained at about 80° C., and the film was annealed for about 1 hour to form a self-assembled film. For the formed film, SEM (scanning electron microscope) image capture was performed. FIG. 3 is an SEM image of the self-assembled film. It can be confirmed that the self-assembled film has formed a vertically oriented cylinder pattern. 

1. A method for producing a polymer film, comprising: annealing a polymer film having a block copolymer at a temperature (T1) on one side of the polymer film and at a temperature (T2) on the opposite side of the polymer film to form a self-assembled structure of the block copolymer, wherein the block copolymer having a polymer segment A and a polymer segment B that is different from the polymer segment A, and wherein the difference (T1−T2) is in a range of 40° C. to 500° C.
 2. The method for producing a polymer film according to claim 1, wherein the self-assembled structure is a sphere, cylinder or lamellar structure.
 3. The method for producing a polymer film according to claim 1, wherein the self-assembled structure is a vertically oriented structure.
 4. The method for producing a polymer film according to claim 1, wherein T1 is maintained in a range of 100° C. to 300° C.
 5. The method for producing a polymer film according to claim 1, wherein the polymer segments A and B are each any one segment selected from the group consisting of a polystyrene segment, a poly(alkyl (meth)acrylate) segment, a polyvinylpyrrolidone segment, a polylactic acid segment, a polyvinylpyridine segment, a polyalkylene oxide segment, a polybutadiene segment, a polyisoprene segment and a polyolefin segment.
 6. The method for producing a polymer film according to claim 1, wherein the polymer segment A satisfies one or more of Conditions 1 to 3 below: Condition 1: it exhibits a melting transition peak or an isotropic transition peak in a range of −80 to 200 in a DSC analysis: Condition 2: it exhibits an X-ray diffraction (XRD) peak having a half-value width in a range of 0.2 to 0.9 nm⁻¹ within a scattering vector (q) range of 0.5 nm⁻¹ to 10 nm⁻¹: Condition 3: it comprises a side chain, wherein the number (n) of chain-forming atoms in the side chain satisfies Equation 1 below with the scattering vector (q): 3 nm⁻¹ to 5 nm⁻¹ =nq/(2×π)  [Equation 11 wherein, n is a number of the chain-forming atoms and q is the smallest scattering vector (q) in which an XRD peak is observed for the block copolymer or the scattering vector (q) in which an XRD peak of the largest peak area is observed.
 7. The method for producing a polymer film according to claim 6, wherein the absolute value of the difference in surface energy between the polymer segments A and B is in a range of 2.5 to 7 mN/m.
 8. The method for producing a polymer film according to claim 1, wherein the polymer segment A comprises a side chain having 8 or more chain-forming atoms.
 9. The method for producing a polymer film according to claim 8, wherein the polymer segment comprises a ring structure and the side chain is substituted on the ring structure.
 10. The method for producing a polymer film according to claim 9, wherein no halogen atom is present in the ring structure.
 11. The method for producing a polymer film according to claim 8, wherein the polymer segment B comprises 3 or more halogen atoms.
 12. The method for producing a polymer film according to claim 11, wherein the polymer segment B comprises a ring structure and the halogen atoms are substituted on the ring structure.
 13. A method for producing a patterned substrate, comprising: forming a polymer film on a substrate, wherein the polymer film comprises a block copolymer having a polymer segment A and a polymer segment B different from the segment A; and annealing the polymer film at a temperature (T1) on one side of the polymer film and at a temperature (T2) on the opposite side of the polymer film, wherein the difference (T1−T2) is in a range of 40° C. to 500° C.
 14. The method for producing a patterned substrate according to claim 13, wherein the polymer film is formed in direct contact with the substrate.
 15. The method for producing a patterned substrate according to claim 13, further comprising: selectively removing any one polymer segment of the block copolymer forming the self-assembled structure to expose a surface of the substrate, the exposed surface of the substrate underlying the portion of the polymer film that is removed.
 16. The method for producing a patterned substrate according to claim 15, further comprising: etching the exposed surface of the substrate using the polymer film as a mask. 